可塑纤维桩在口腔残根修复中的应用效果观察(1)
[摘要] 目的 探讨口腔残根修复中可塑纤维桩的应用效果。 方法 选取2014年2月～2015年1月我院收治的口腔残根修复患者60例76颗病牙，根据修复方法不同分为观察组和对照组，观察组进行可塑纤维桩进行口腔残根修复，对照组采用传统金属桩修复，观察两组患者6个月后的应用效果。 结果 观察组修复成功率明显高于对照组，观察组修复后松动脱落、折断情况明显低于对照组，两组差异具有统计学意义(P<0.05)。 结论 可塑纤维桩可有效修复口腔残根，成功率高，效果显著，值得关注。
[关键词] 口腔残根；修复；金属桩；可塑纤维桩
[中图分类号] R783.3 [文献标识码] B [文章编号] 1673-9701(2015)26-0059-03
Application effect observation of plastic fiber post in oral residual root repair
WU Guohua
Department of Stomatology， Xiamen Xianyue Hospital， Fujian， Xiamen 361000， China
[Abstract] Objective To evaluate the application effect of plastic fiber post in oral residual root repair. Methods Sixty patients (76 affected teeth) who received oral residual root repair in our hospital from February 2014 to January 2015 were selected and divided into the observation group and the control group according to different repair methods. The observation group was given plastic fiber post for oral residual root repair and the control group was given traditional metal post repair. The application effects of the two groups 6 months later were observed. Results The observation group was significantly higher than the control group in the successful repair rate and the observation group was significantly lower than the control group in the occurrence of looseness， detachment and break， with statistically significant differences (P<0.05). Conclusion Plastic fiber post can effectively repair oral residual root， has high success rate and shows remarkable effects， which is worthy of attention.
[Key words] Oral residual root； Repair； Metal post； Plastic fiber post
口腔修复是口腔医学中的一个重要分支，主要是对牙齿的缺损进行治疗，也可利用人工修复体对牙周病、颌面组织缺损进行治疗[1]。随着医疗水平的发展，残根残冠基本上可以长期保留，而且经过有效的修复，残根残冠基本上可以恢复牙齿原来的面貌，既美观又实用。目前，运用可塑性纤维桩在残根残冠修复的应用越来越广泛，其具有弹性好、不易出现劈裂、粘贴紧、抗折及抗腐蚀性能强、可重复修复等优点，弥补了传统金属桩残根残冠修复的不足[2]。为了进一步探讨可塑纤维桩在口腔残根修复中的应用，本研究选取2014年2月～2015年1月60例腔残根修复患者进行分析，现报道如下。
1 资料与方法
1.1 临床资料
选取2014年2月～2015年1月我院收治的口腔残根修复患者60例(76颗病牙)，将患者随机分为两组，观察组和对照组各30例(38颗病牙)。其中观察组男20例，女10例，年龄22～70岁，平均(39.1±2.8)岁，平均病程(0.87±0.13)年。对照组男18例，女12例，年龄21～72岁，平均(38.7±2.9)岁， 平均病程(0.91±0.12)年。所选患者均需进行修复治疗，两组患者在年龄、性别、病程方面差异无统计学意义(P>0.05)，见表1。
表1 两组患者一般资料比较
注：与对照组比较，*P>0.05
1.2 纳入及排除标准
纳入标准：口腔残根符合桩核冠修复、无慢性炎症及已进行完善根管治疗的患者。排除标准：残根有明显的感染和有慢性炎症者；严重的根尖吸收，牙槽骨吸收超过根长的1/3以上者；根管壁已有侧穿、咬合紧和牙根长度不足者。
1.3 方法
对照组患者应用传统金属桩进行牙根残留修复，观察组患者应用可塑纤维桩进行修复治疗，具体操作如下：进行修复前准备好所需物品，高强度纤维、纤维套装及全瓷系统。将龋坏的牙体组织去除，保留牙体软组织，预留2 mm的牙本质肩颌。对患者拍X线进行牙体残根测量，对不完整的根管进行彻底治疗，完成的根道深度长约1/2～3/4，预留3～5 mm的根尖封闭区。根管制备，用橡皮障隔离患牙，用预成钻去除牙胶充填物，选择合适的完成钻制备成根管。测量好根道距离后采取合适的纤维尺寸，纤维长度需超出5 mm。根据牙齿冠部的缺损对纤维的位置进行适当调整，然后进行光照，固化维持20 s左右，再将纤维桩取下进行光照，需要固化40 s，稳定好根内形态。对已经成型的纤维桩固定在根道内涂上粘贴剂，待桩核硬化后，进行排龈处理，制作印模，在印模中做石膏模型，做好修复体进行试戴。根据试戴情况进行调整，然后将其粘贴好[3-5]。修复完后在半年内进行复查，出现异常及时处理。, 百拇医药(吴国华)
[关键词] 口腔残根；修复；金属桩；可塑纤维桩
[中图分类号] R783.3 [文献标识码] B [文章编号] 1673-9701(2015)26-0059-03
Application effect observation of plastic fiber post in oral residual root repair
WU Guohua
Department of Stomatology， Xiamen Xianyue Hospital， Fujian， Xiamen 361000， China
[Abstract] Objective To evaluate the application effect of plastic fiber post in oral residual root repair. Methods Sixty patients (76 affected teeth) who received oral residual root repair in our hospital from February 2014 to January 2015 were selected and divided into the observation group and the control group according to different repair methods. The observation group was given plastic fiber post for oral residual root repair and the control group was given traditional metal post repair. The application effects of the two groups 6 months later were observed. Results The observation group was significantly higher than the control group in the successful repair rate and the observation group was significantly lower than the control group in the occurrence of looseness， detachment and break， with statistically significant differences (P<0.05). Conclusion Plastic fiber post can effectively repair oral residual root， has high success rate and shows remarkable effects， which is worthy of attention.
[Key words] Oral residual root； Repair； Metal post； Plastic fiber post
口腔修复是口腔医学中的一个重要分支，主要是对牙齿的缺损进行治疗，也可利用人工修复体对牙周病、颌面组织缺损进行治疗[1]。随着医疗水平的发展，残根残冠基本上可以长期保留，而且经过有效的修复，残根残冠基本上可以恢复牙齿原来的面貌，既美观又实用。目前，运用可塑性纤维桩在残根残冠修复的应用越来越广泛，其具有弹性好、不易出现劈裂、粘贴紧、抗折及抗腐蚀性能强、可重复修复等优点，弥补了传统金属桩残根残冠修复的不足[2]。为了进一步探讨可塑纤维桩在口腔残根修复中的应用，本研究选取2014年2月～2015年1月60例腔残根修复患者进行分析，现报道如下。
1 资料与方法
1.1 临床资料
选取2014年2月～2015年1月我院收治的口腔残根修复患者60例(76颗病牙)，将患者随机分为两组，观察组和对照组各30例(38颗病牙)。其中观察组男20例，女10例，年龄22～70岁，平均(39.1±2.8)岁，平均病程(0.87±0.13)年。对照组男18例，女12例，年龄21～72岁，平均(38.7±2.9)岁， 平均病程(0.91±0.12)年。所选患者均需进行修复治疗，两组患者在年龄、性别、病程方面差异无统计学意义(P>0.05)，见表1。
表1 两组患者一般资料比较
注：与对照组比较，*P>0.05
1.2 纳入及排除标准
纳入标准：口腔残根符合桩核冠修复、无慢性炎症及已进行完善根管治疗的患者。排除标准：残根有明显的感染和有慢性炎症者；严重的根尖吸收，牙槽骨吸收超过根长的1/3以上者；根管壁已有侧穿、咬合紧和牙根长度不足者。
1.3 方法
对照组患者应用传统金属桩进行牙根残留修复，观察组患者应用可塑纤维桩进行修复治疗，具体操作如下：进行修复前准备好所需物品，高强度纤维、纤维套装及全瓷系统。将龋坏的牙体组织去除，保留牙体软组织，预留2 mm的牙本质肩颌。对患者拍X线进行牙体残根测量，对不完整的根管进行彻底治疗，完成的根道深度长约1/2～3/4，预留3～5 mm的根尖封闭区。根管制备，用橡皮障隔离患牙，用预成钻去除牙胶充填物，选择合适的完成钻制备成根管。测量好根道距离后采取合适的纤维尺寸，纤维长度需超出5 mm。根据牙齿冠部的缺损对纤维的位置进行适当调整，然后进行光照，固化维持20 s左右，再将纤维桩取下进行光照，需要固化40 s，稳定好根内形态。对已经成型的纤维桩固定在根道内涂上粘贴剂，待桩核硬化后，进行排龈处理，制作印模，在印模中做石膏模型，做好修复体进行试戴。根据试戴情况进行调整，然后将其粘贴好[3-5]。修复完后在半年内进行复查，出现异常及时处理。, 百拇医药(吴国华)